Clinical performance of one-step self-etch adhesives applied actively in cervical lesions: 24-month clinical trial.

OBJECTIVES: To evaluate the clinical performance of two one-step self-etch adhesives in noncarious cervical lesions (NCCL) under active or passive application mode. METHODS: Thirty-one patients with four NCCL were enrolled in this study. One hundred and twenty-four restorations were placed according to one of the following conditions: 1) Adper Prompt L-Pop (AP), active application (APA); 2) AP, passive application (APP); 3) Xeno III (XE), active application (XEA), or 4) XE, passive application (XEP). The restorations were evaluated by the FDI World Dental Federation criteria at baseline and after six, 12, and 24 months of clinical service. The effects of adhesive, mode of application, and recall period were assessed via mixed generalized linear model (α=0.05). RESULTS: The adhesive AP and the passive application mode showed significantly higher marginal staining than did XE and active application, respectively (p<0.05). With regard to the retention rates, the active application mode yielded higher retention rates at the 24-month recall compared to the passive application, regardless of the material. The individual retention rates (95% confidence interval) of both adhesives in the active application mode were the same, 96.8% (83.8-99.4%), while in the passive application rates were 87.1% (71.2-94.9%) and 80.7% (63.7-90.8%) for XE and AP, respectively. CONCLUSIONS: The active application improved the retention rates of both adhesives after 24 months and minimized the marginal staining at enamel margins.

Chlorhexidine-containing acid conditioner preserves the longevity of resin-dentin bonds.

The current study evaluated the effect of 2% chlorhexidine digluconate (CHX) on the immediate and six-month resin-dentin bond strength (BS) and nanoleakage pattern (NL) of etch-and-rinse adhesives when applied in aqueous or associated to the phosphoric acid conditioner. The occlusal enamel of 42 caries-free extracted molars was removed in order to expose a flat dentin surface. In groups 1 and 2 (control-C), the surfaces were acid etched with conventional phosphoric acid, and the adhesives Prime&Bond NT (PB) and Adper Single Bond 2 (SB) were applied after rinsing, drying and rewetting with water. In groups 3 and 4 (Ac/CHX), the adhesives were applied in a similar manner, however, a 2% CHX-containing acid was previously applied. In groups 5 and 6 (CHX), the adhesives were applied according to the control group; however, the rewetting procedure was performed with an aqueous solution of 2% CHX for 60 seconds. Composite buildups (Opallis, FGM) were constructed incrementally, and the specimens were longitudinally sectioned in the "x" and "y" directions to obtain bonded sticks (0.8 mm2) to be tested in tension at 0.5 mm/minute immediately or after six months of water storage. For NL, two bonded sticks from each tooth were coated with nail varnish, placed in silver nitrate and polished down with SiC paper. Resin-dentin interfaces were analyzed by EDX-SEM. The BS and NL data from each adhesive was submitted to two-way repeated measures ANOVA and Tukey's test (alpha=0.05). After six months of water storage, significant reductions in BS were observed for both adhesives in the control group (p<0.05). When Ac/CHX or CHX was used, no significant reductions in BS were observed for both systems. Nanoleakage was more evident in the control group than in the experimental groups (p<0.05), even after six months. The use of CHX in an aqueous solution or associated with the acid conditioner was effective for reducing degradation of resin-dentin bonds after six months of water storage.